| Name | Item | Use |
|---|---|---|
| Environmentally friendly halogen-free thermoplastic polyurethane elastomer cable compound | YHS70023 | High strength, high abrasion resistance, water resistance, oil resistance, used for power lines, data lines, spring wires, etc. |
| Environmentally friendly halogen-free flame-retardant thermoplastic polyurethane elastomer cable compound | YHS70023Z | High flame retardant, high strength, wear resistance, oil resistance, used for flame retardant oil well cables, marine cables, power lines, etc. |
| 125 ℃ Irradiation Crosslinked Polyurethane Elastomer Cable Compound | YHS70023-125 | High strength, high oil resistance, high wear resistance, used for oil resistant locomotive lines, brake lines, oil wells and ship lines |
| 125 ℃ halogen-free flame-retardant radiation crosslinked polyurethane elastomer cable compound | YHS70023Z-125 | High flame retardant, high oil resistance, high wear resistance, used for oil resistant locomotive lines, brake lines, oil wells and ship lines |
Environmentally friendly polyurethane elastomer cable material series products are based on polyurethane elastomer (TPU), adding high-efficiency flame retardants, antioxidants, cross-linking sensitizers and other processing aids. After mixing, plasticizing, Granulated. The product not only has the advantages of high heat resistance, high strength, high wear resistance, solvent resistance, etc., but also can increase the special properties such as different hardness, weather resistance, UV resistance, matte matte, etc. according to customer needs. This product is made by extrusion The products are exquisite in appearance, smooth in surface, comfortable in feel, and do not contain halogen, heavy metals, phthalates, and comply with EU RoHS, REACH and other environmental protection directives.
When the storage time is long or the environment is humid, or the product surface requirements are high, the pellets can be dried in a hot air hopper at 60-70 ℃ for 1 to 2 hours before use.
It is recommended to use screw extrusion with L / D≥25 and compression ratio of 2.0 ~ 2.5: 1. The screw should be cleaned before extrusion to ensure the cleanliness of the product. It is recommended to use 80 mesh or 100 mesh filter to avoid impurities in the extrusion process, while ensuring the melt pressure to obtain a good appearance and material compactness. Because the difference between the actual temperature of the melt and the value indicated by the temperature control meter varies with the type of extruder, users are requested to choose the appropriate temperature according to the specific situation of the extruder used. The following temperatures can be used as a reference for commissioning:
| Position | Cylinder I | Cylinder Ⅱ | Cylinder Ⅲ | Cylinder Ⅳ | Cylinder Ⅴ | Head and mold |
|---|---|---|---|---|---|---|
| Temperature | 140±10 | 160±10 | 165±10 | 170±10 | 175±10 | 175±10 |
(25 ± 0.2) kg / bag, inner aluminum plastic composite bag, outer kraft paper bag (or customer specified packaging)
Stored in dry and ventilated place
Prevent sun, rain and water
Storage period is 6 months
| Test Project | Units | Typical values | |||
|---|---|---|---|---|---|
| YHS70023 | YHS70023Z | YHS70023-125 | YHS70023Z-125 | ||
| Density | g/cm3 | 1.10 | 1.25 | 1.12 | 1.28 |
| Hardness | Shore A | 70-95 | 75-98 | 70-98 | 75-98 |
| Original tensile strength | MPa | 31.0 | 5.0 | 7.0 | 12.0 |
| Original elongation at break | % | 600 | 380 | 380 | 280 |
| Air thermal aging | ℃ ×h | 136×168 | 158×168 | ||
| Change rate of tensile strength | % | -10 | -15 | -15 | -16 |
| Change rate of elongation at break | % | -13 | -12 | -16 | -18 |
| Low temperature impact embrittlement temperature | ℃ | -40 pass | -40 pass | -40 pass | -40 pass |
| 20°C volume resistivity | Ω.cm | 2.5×1013 | 3.0×1013 | 8.0×1013 | 8.0×1013 |
| Oxygen Index | % | - | 26 | - | 28 |
| (902#)Resistance to mineral oil (902 #) | ℃ ×h | 100×70 | |||
| Change rate of tensile strength | % | - | - | -25 | -22 |
| Change rate of elongation at break | % | - | - | -20 | -18 |
| Fuel resistant oil (903 #) | ℃ ×h | 70×168 | |||
| Change rate of tensile strength | % | - | - | -22 | -20 |
| Change rate of elongation at break | % | - | - | -18 | -16 |
| Thermal deformation (90 ° C * 4H) | % | 15 | 12 | 9 | 7 |
| Halogen acid gas content | mg/g | 0 | 0 | 0 | 0 |
| Flame retardant rating (UL94) | - | HB | FT-2 | HB | VW-1 |
Note: The above data is a typical value obtained by testing the product and is not a standard for testing restrictions.