CONTACT US
Name | Item | Use |
---|---|---|
125℃ halogen-free flame-retardant TPV elastomer cable compound | YHS70026-125 | 85-90AHalogen-free flame retardant, excellent heat aging performance, high resilience, no irradiation required, hardness 85-90A |
125 ℃ low halogen flame retardant TPV elastomer cable compound | YHS70026D-125 | 含卤、高阻燃、耐热性能优越,高回弹性、 硬度 75-90A 可调,用于汽车线、机车线、 电机引接线等 |
TPV elastomer cable material series products are based on a blend of TPV with polypropylene and EPDM as the main materials and dynamically vulcanized as the base material, adding high-efficiency flame retardants, antioxidants, and other processing Additives are made by mixing, plasticizing and granulating. The product not only has the advantages of high heat resistance, high strength, solvent resistance, etc., but also can increase the special properties such as different hardness, weather resistance, UV resistance, matte matte, etc. according to customer needs. , The surface is smooth and comfortable, and it does not contain heavy metals and phthalates. It complies with EU RoHS, REACH and other environmental protection directives.
When the storage time is long or the environment is humid, or the product surface requirements are high, the pellets can be dried in a hot air hopper at 60-70 ℃ for 1 to 2 hours before use.
It is recommended to use screw extrusion with L / D≥25 and compression ratio of 1.5 ~ 2.0: 1. The screw should be cleaned before extrusion to ensure the cleanliness of the product. It is recommended to use 80 mesh or 100 mesh filter to avoid impurities in the extrusion process, while ensuring the melt pressure to obtain a good appearance and material compactness. Because the difference between the actual temperature of the melt and the value indicated by the temperature control meter varies with the type of extruder, users are requested to choose the appropriate temperature according to the specific situation of the extruder used. The following temperatures can be used as a reference for commissioning:
Position | Cylinder I | Cylinder Ⅱ | Cylinder Ⅲ | Cylinder Ⅳ | Cylinder Ⅴ | Head and mold |
---|---|---|---|---|---|---|
Temperature | 150±10 | 175±10 | 185±10 | 195±10 | 200±10 | 210±10 |
(25 ± 0.2) kg / bag, inner aluminum plastic composite bag, outer kraft paper bag (or customer specified packaging)
Stored in dry and ventilated place
Prevent sun, rain and water
Storage period is 6 months
Test Project | Units | Typical values | |
---|---|---|---|
YHS70026-125 | YHS70026D-125 | ||
Density | g/cm3 | 1.25 | 1.18 |
Original tensile strength | MPa | 11.5 | 14.3 |
Original elongation at break | % | 210 | 350 |
Air thermal aging | ℃ ×h | 158×168 | |
Change rate of tensile strength | % | -15 | -14 |
Change rate of elongation at break | % | -18 | -16 |
Low temperature impact embrittlement temperature | ℃ | -40 pass | -40 pass |
20°C volume resistivity | Ω.cm | 2.0×1014 | 2.0×1014 |
Dielectric strength | MV/m | 22 | 25 |
Oxygen Index | % | 30 | 31 |
Thermal deformation (90 ° C * 4H) | % | 9 | 7 |
Halogen acid gas content | mg/g | 0 | - |
Flame retardant rating (UL94) | - | FT-2 | VW-1 |
Note: The above data is a typical value obtained by testing the product and is not a standard for testing restrictions.